Physical Properties Test Standard Unit Value Hardness ASTM D2240 shore A 96 Hardness ASTM D2240 shore D 51 Density ASTM D792 g/cm3 1.19 Tensile strength ASTM D412 (500mm/min) MPa 42 100% modulus ASTM D412 (500mm/min) MPa 14.5 300% modulus ASTM D412 (500mm/min) MPa30 Elongation at Confractus ASTM D412 (500mm / Min) DCC lacrimam Fortitudo ASTM D264 (500mm / MIN (Modum 24h) ASTM D395 (Modum B. 24. DC95 (Modum B. 24. DECRIFICUS TR10 GB / T7758 - MMII ℃ - XXX Minimum Temperatus DECREMENTUM TRIC3 GB / T (VII) DCCLVIII - MMII ℃ - XX humilis temperatus DECREMENTUM TR50 GB / T (VII) DCCLVIII - MMII ℃ -

Technical parametri rated valorem test methodo

Unputched impulsum vires 83KJ / M² (XXIII ℃) ISO CLXXIX / 1ea

46KJ / M² (- XX ℃ ISO CLXXIX / 1ea

Impact fortitudo cantilever trabs noth 78KJ / M² (XXIII ℃) ISO CLXXIX / 1ea

33KJ / M² (- XX ℃ ISO CLXXIX / 1ea

Temperature range - LV ~ CLXXX ℃ ASTM D1525

Tensile modulus 1900mpa ISO DXXVII - II

Tensile fortitudo 550MA ISO (XII) LXXXVI

Flexural Modulum 1750MPA ISO DXXVII - II

Litus Deness (Shosed) LXVIII ASTM D792

Density 1.12 ISO MCLXXXIII

Reciprocating Volo 15M / S

Working temperature: Polyformaldehyde POM -30-100 ℃, phenolic resin PF -55-120 ℃, filled PTFE+40% copper powder -200-260 ℃ Working temperature: Polyformaldehyde POM -30-100 ℃, phenolic resin PF -55-120 ℃, filled PTFE+40% copper powder -200-260 ℃ Working temperature: Polyformaldehyde POM -30-100 ℃, phenolic resin PF -55-120 ℃, filled PTFE+40% copper powder -200-260 ℃ Working temperature: Polyformaldehyde POM -30-100 ℃, phenolic resin PF -55-120 ℃, filled PTFE+40% copper powder -200-260 ℃ Working temperature: Polyformaldehyde POM -30-100 ℃, Phenolic resin PF -55-120 ℃, filled PTFE+40% copper powder -200-260 ℃, working temperature: POM -30-100 ℃, phenolic resin PF -55-120 ℃, filled PTFE+40% copper powder -200-260 ℃, working temperature: POM -30-100 ℃, phenolic resin PF -55-120 ℃, repleti ptfe + XL% aeris pulveris - CC - CCLX ℃, working temperatus: pom - XXX - Cf ℃, phenolic resinae pf - LV% aeris pulveris - CC - ℃